Semitron™ CMP XL20 PAI was developed from a proprietary polyamide-base resin and offers wear life more than 20 times that of standard PPS in all CMP chemistry environments. This material has the best combination of wear life and mechanical strength and stiffness, ideal for the most demanding applications and in extreme process environments.
EIGENSCHAPPEN
High strength and stiffness promotes fewer edge defects and better uniformity
Good chemical and creep resistance
Excellent wear life
Dimensionaal stabiel
Outperforms PPS up to 20x in most processes
Thermische eigenschappen
Eigendom
Waarde
Warmteafbuigingstemperatuur bij 1,8MPa (264 psi) (ºC)
Continu toelaatbare bedrijfstemperatuur in lucht
260
Mechanische eigenschappen
Eigendom
Waarde
Treksterkte (MPa)
Elasticiteitsmodulus (MPa)
Drukspanning bij 1% nominale rek (MPa)
Drukspanning bij 2% nominale rek (MPa)
Drukspanning bij 5% nominale rek (MPa)
Buigsterkte (MPa)
Charpy Ingeslagen Impact (kJ/m²)
Chemische eigenschappen
Eigendom
Waarde
Heet water / stoom
Beperkt
Zuren, Zwak
Aanvaardbaar
Zuren, sterk (pH 1-3)
Beperkt
Alkaliën, Zwak
Beperkt
Alkaliën, sterk (pH 11-14)
Niet acceptabel
Koolwaterstoffen - Aromatische
Aanvaardbaar
Koolwaterstoffen - Alifatische
Aanvaardbaar
Ketonen, Esters
Aanvaardbaar
Gechloreerde oplosmiddelen
Aanvaardbaar
Alcoholen
Aanvaardbaar
Anorganische zoutoplossingen
Aanvaardbaar
Elektrische eigenschappen
Eigendom
Waarde
Diëlektrische sterkte (kV/mm)
Certificeringseigenschappen
Eigendom
Waarde
FDA
Niet in overeenstemming
Europese voedselgoedkeuring
Niet in overeenstemming
NSF
Niet in overeenstemming
3A-SSI
Niet in overeenstemming
Canada AG
USDA
Niet in overeenstemming
Ontvlambaarheid (UL-classificatie)
V-0
Medisch gebruik
Diverse eigenschappen
Eigendom
Waarde
Basismateriaal
PAI
Merk Familie
Kleuren
Groen
Dichtheid (g/cm3)
Waterabsorptie na 24 uur onderdompeling in water (%)