Ketron™ HPV PEEK shapes are carbon fiber-reinforced polyetheretherketone materials with graphite and PTFE lubricants, giving them the lowest coefficient of friction and the best machinability of all PEEK materials. Due to Ketron™ HPV PEEK’s combination of low wear and friction and high LPV, this grade is often chosen as a solution for service bearings, bushings, insulators, valves and seals.
EIGENSCHAFTEN
carbon fiber-reinforced with graphite and PTFE lubricants
Excellent wear resistance
High limiting pressure velocity (LPV)
High mechanical strength and stiffness
Low coefficient of friction (COF)
Thermische Eigenschaften
Eigentum
Wert
Wärmeverformung Temperatur bei 1,8MPa (264 psi) (ºC)
195
Dauernd zulässige Betriebstemperatur in Luft
250
Mechanische Eigenschaften
Eigentum
Wert
Zugfestigkeit (MPa)
78
Zug-Elastizitätsmodul (MPa)
5,900
Druckspannung bei 1% Nenndehnung (MPa)
46
Druckspannung bei 2% Nenndehnung (MPa)
80
Druckspannung bei 5% Nenndehnung (MPa)
120
Biegefestigkeit (MPa)
125
Charpy-Kerbschlagzähigkeit (kJ/m²)
3.0
Chemische Eigenschaften
Eigentum
Wert
Heißwasser/Dampf
Annehmbar
Säuren, schwache
Annehmbar
Säuren, stark (pH 1-3)
Begrenzt
Alkalien, Schwache
Annehmbar
Alkalien, stark (pH 11-14)
Annehmbar
Kohlenwasserstoffe - aromatisch
Annehmbar
Kohlenwasserstoffe - Aliphatische
Annehmbar
Ketone, Ester
Annehmbar
Chlorierte Lösungsmittel
Annehmbar
Alkohole
Annehmbar
Anorganische Salzlösungen
Annehmbar
Elektrische Eigenschaften
Eigentum
Wert
Durchschlagfestigkeit (kV/mm)
Eigenschaften der Zertifizierung
Eigentum
Wert
FDA
Nicht konform
Europäische Lebensmittelzulassung
Nicht konform
NSF
Nicht konform
3A-SSI
Nicht konform
Kanada AG
USDA
Nicht konform
Entflammbarkeit (UL-Bewertung)
V-0
Medizinische Verwendung
Verschiedene Eigenschaften
Eigentum
Wert
Grundmaterial
PEEK
Marke Familie
Farben
Black
Dichte (g/cm3)
1.45
Wasserabsorption nach 24 Stunden Eintauchen in Wasser (%)