Duratron™ T4501 PAI possesses high compressive strength and excellent wear resistance, making it a great performer in general purpose wear and friction applications. This grade is similar in composition to Duratron™ T4301, offering a very high flexural modulus and exhibiting little to no stick-slip and is able to endure harsh thermal, chemical and stress conditions. Duratron™ T4501 PAI is a reliable solution for parts requiring larger dimensions and high compressive strength.
EIGENSCHAFTEN
Available in larger dimensions
High compressive strength and flexural modulus
Low wear and little-to-no stickslip
Suitable for harsh thermal, chemical and stress conditions
Thermische Eigenschaften
Eigentum
Wert
Wärmeverformung Temperatur bei 1,8MPa (264 psi) (ºC)
280
Dauernd zulässige Betriebstemperatur in Luft
260
Mechanische Eigenschaften
Eigentum
Wert
Zugfestigkeit (MPa)
110
Zug-Elastizitätsmodul (MPa)
5,500
Druckspannung bei 1% Nenndehnung (MPa)
39
Druckspannung bei 2% Nenndehnung (MPa)
72
Druckspannung bei 5% Nenndehnung (MPa)
130
Biegefestigkeit (MPa)
155
Charpy-Kerbschlagzähigkeit (kJ/m²)
4.0
Chemische Eigenschaften
Eigentum
Wert
Heißwasser/Dampf
Begrenzt
Säuren, schwache
Annehmbar
Säuren, stark (pH 1-3)
Begrenzt
Alkalien, Schwache
Begrenzt
Alkalien, stark (pH 11-14)
Nicht akzeptabel
Kohlenwasserstoffe - aromatisch
Annehmbar
Kohlenwasserstoffe - Aliphatische
Annehmbar
Ketone, Ester
Annehmbar
Chlorierte Lösungsmittel
Annehmbar
Alkohole
Annehmbar
Anorganische Salzlösungen
Annehmbar
Elektrische Eigenschaften
Eigentum
Wert
Durchschlagfestigkeit (kV/mm)
Eigenschaften der Zertifizierung
Eigentum
Wert
FDA
Nicht konform
Europäische Lebensmittelzulassung
Nicht konform
NSF
Nicht konform
3A-SSI
Nicht konform
Kanada AG
USDA
Nicht konform
Entflammbarkeit (UL-Bewertung)
V-0
Medizinische Verwendung
Verschiedene Eigenschaften
Eigentum
Wert
Grundmaterial
PAI
Marke Familie
Farben
Black
Dichte (g/cm3)
1.45
Wasserabsorption nach 24 Stunden Eintauchen in Wasser (%)